Absorbent structure designed for absorbing body fluids

ABSTRACT

An absorbent structure designed for use in absorbent pads such as diapers is disclosed. According to a first aspect of the invention, absorbent pads are provided which comprise at least two layers of cellulosic fibers (fluff) of different densities or average pore size ranges. When the absorbent structure is incorporated in a diaper, the lower density element extends to the full length and width dimensions of the normal absorbent component of the diaper. The higher density element lies beneath at least a portion of the lower density element. According to various embodiments of the present invention, it can run as a strip from the target zone to the back waist of a diaper, it can run along a central portion extending the whole length of the diaper, or it can underlie the entirety of the lower density element. The higher density element (or the element having a lower average pore size) wicks waste fluid from a lower central portion of the diaper, and thereby transports the fluid upwardly and also transfers it to the lower density element (or the element of greater average pore size). According to a second aspect of the invention, which may be incorporated with the first aspect just described, a portion of superabsorbent material is placed beneath the higher density layer, (or layer of lower average pore size), such that an additional reservoir for absorbing waste fluid is provided.

CROSS REFERENCE TO RELATED APPLICATIONS

This is a divisional of copending, commonly assigned U.S. patent application Ser. No. 07/083,475 filed Aug. 6, 1987, by Leo J. Bernardin, now U.S. Pat. No. 5,000,650 which is a continuation of copending, commonly assigned U.S. patent application Ser. No. 06/886,780 filed Jul. 17, 1986, by Leo J. Bernardin, now U.S. Pat. No. 4,699,619, which is a continuation-in-part of copending, commonly assigned U.S. patent application Ser. No. 06/656,384 filed Aug. 31, 1984, by Leo J. Bernardin, now abandoned, which is a continuation-in-part of copending, commonly assigned U.S. patent application Ser. No. 06/599,882, filed Apr. 13, 1984, by Leo J. Bernardin, now abandoned.

BACKGROUND OF THE INVENTION

This invention relates to an absorbent structure such as may be used in a disposable diaper. This is a continuation in part of U.S. patent application Ser. No. 656,384, filed Aug. 31, 1984, by the same inventor, which is a continuation in part of U.S. patent application Ser. No. 599,882, filed Apr. 13, 1984, also be the same inventor.

Disposable diapers generally include an inner, liquid permeable liner that lies closest to the wearer's skin. An outer, liquid impermeable cover is disposed at the outside of the diaper, furthest away from the wearer. In between the liner and the cover is a fibrous liquid absorbent material or batt.

In general, the most economical liquid absorbent material for use in disposable diapers is cellulosic fibers such as comminuted wood pulp, commonly known in the art as "fluff pulp," or simply "fluff " Batts made from these fibers have a low density and a high capacity for absorbing fluids, but their wicking ability is very poor Thus, the low central crotch portion of the diaper as worn tends to become very wet when waste fluids are released thereupon, while the fluff included in the higher portions of the diaper (as worn) can remain dry with its absorbent capacity unused.

Several problems are posed by this First, it is uneconomical to line a diaper with fluff, the majority of which will be wasted. Further, there can be leakage from the liquid saturated central portion of the diaper Still further, this concentration of liquid localized in one region of the diaper can cause discomfort to the wearer of the diaper.

One prior art approach noted by Sigl in U.S. Pat. No. 4,213,459 to avoid some of these problems is to decrease the pore size such that the improved capillary action of the pores overcomes the force of gravity sufficiently to cause the waste liquid to move upwardly in the diaper. However, it has been noted that the total absorption capacity is reduced by reducing the average pore size. Nevertheless, the use of this approach to achieve a better distribution of fluid throughout the available area in the diaper has generally been the approach of choice despite the resulting loss in absorption capacity.

A further step was taken towards the solution of these problems by Sigl (in U.S. Pat. No 4,213,459, assigned to the assignee of the present invention). Sigl discloses providing a localized area of increased density fluff in the batt for wicking waste fluid to a higher portion of the diaper Although this presented an advance in the art, it was not without drawbacks First, the surface of the diaper nearest the wearer's skin directly beneath the lining becomes soaked Further, the only places where liquid could be transferred from the lower density material to the higher density material were at the borders or edges where the lower density material adjoins the higher density material Thus, it was suggested in that patent that the areas around the densified region of the batt should remain undensified

The present invention provides a further advancement in the art, as will be fully explained below.

SUMMARY OF THE INVENTION

This invention is directed to an improved absorbent structure designed for use in absorbent pads such as diapers, for absorbing body fluids.

According to a first aspect of this invention, the absorbent pad or batt comprises at least two layers of cellulosic fibers of different densities or average pore sizes. In a disposable diaper having a body facing, liquid permeable liner, an outer liquid impermeable cover and a liquid absorbing material therebetween, the improvement of this invention is directed to providing as the absorbing material, a first layer of cellulosic fiber having a first density or average pore size and underlying the permeable lining. A second layer of cellulosic fiber formed substantially separately from the first layer and having a higher density or a lower average pore size than the first layer underlies at least a portion of the first layer.

According to a second aspect of the invention, a superabsorbent material is inserted adjacent the higher density layer of cellulosic fiber According to one preferred embodiment, the superabsorbent material is sandwiched between two densified layers of cellulosic fiber, both of which are disposed beneath the lower density layer. According to another preferred embodiment, the superabsorbent material underlies the second layer of cellulosic fiber.

The first aspect can be used alone or in combination with the second aspect Objects and advantages of the invention will best be understood with reference to the following detailed description read in connection with the drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective plan view of a first preferred embodiment of the invention without the superabsorbent material included therein.

FIG. 2 is a longitudinal cross-sectional view taken along line 2--2 of FIG. 1.

FIG. 3 is a perspective plan view of a second preferred embodiment of the present invention, without the superabsorbent included therein.

FIG. 4 is a longitudinal cross-sectional view taken along line 4--4 of FIG. 3.

FIG. 5 is a perspective plan view with several cutaway portions of a third preferred embodiment of the present invention without the superabsorbent material included therein.

FIG. 6 is a perspective plan view of a fourth preferred embodiment of the present invention, including a portion of superabsorbent material incorporated therein.

FIG. 7 is a longitudinal cross-sectional view taken along line 7--7 of FIG. 6.

FIG. 8 is a perspective plan view of a fifth preferred embodiment of the present invention including a portion of superabsorbent material incorporated therein.

FIG. 9 is a longitudinal cross-sectional view taken along line 9--9 of FIG. 8

FIG. 10 is an absorbency profile for the control diaper tested in Example 1.

FIG. 11 is an absorbency profile for the diaper containing one ply of compressed fluff in addition to the regular fluff component as discussed in Example 1.

FIG. 12 is an absorbency profile for the diaper containing two plies of compressed fluff in addition to the regular fluff component as discussed in Example 1.

FIG. 13 is the absorbency profile for the diaper containing three plies of compressed fluff in addition to the regular fluff component as describe in Example 1.

FIG. 14 is the absorbency profile for the diaper containing two plies of compressed fluff plus a portion of superabsorbent material as described in Example 1.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

Turning now to the drawings, the disposable diaper 1 in which the present invention is embodied comprises generally a body facing, liquid permeable liner 2, an outer liquid impermeable cover 3, and a liquid absorbing material indicated generally as 4 therebetween. The focus of this invention is directed to the liquid absorbing material 4. The liquid absorbing material 4 comprises a first, lower density layer 5 of cellulosic fibers such as comminuted wood pulp (fluff) which lies beneath the inner liner 2. A second, higher density layer 6 of fluff lies beneath at least a portion of the first lower density layer 5 such that waste fluid can be transferred from the lower density layer 5 to the higher density layer 6. Thus, a lower surface 15 of the lower density layer 5 should be contiguous with at least a portion of an upper surface 16 of the higher density layer 6. However, a tissue layer can be placed between the layers 5 and 6 without departing from the scope of this invention.

Predominantly softwood pulp fluff can be used for each of the layers 5 and 6. Alternatively, a layer of predominantly softwood fluff can be used for the layer 5 and a layer of preponderantly hardwood fluff can be used for the layer 6, in which case it is the average pore size and not necessarily the density that varies between the layers 5 and 6, as will shortly be explained. For the purposes of this disclosure and the accompanying claims, "predominantly" is intended to mean at least about 80% while "preponderantly" is intended to mean at least about 50%

In the first preferred embodiment shown in FIGS. 1 and 2, the higher density layer 6 is formed as a strip extending from a target area 7, where liquid waste will initially accumulate, to an upper edge 8 towards the back of the diaper. The higher density layer 6 draws waste fluid from the lower density layer 5 in the target area 7 upwardly towards the edge 8 at the back of the diaper 1. Further, along upper regions 18 of the higher density layer 6 towards the upper edge 8 there is, surprisingly, substantial fluid transfer back from the higher density layer 6 to the lower density layer 5. It is important to note that although this flowback occurs from the higher density layer 6 to the lower density layer 5, the lower density layer 5 only draws sufficient fluid to satisfy its unsaturated capillary forces proximate to the higher density layer 6, where there is an overlap in pore sizes such that the smallest pores in the lower density layer 5 are smaller than the largest pores in the higher density layer 6. The lower density layer 5 drains fluid from the higher density layer 6 but does not become soaked, with the advantage that the wearer's comfort is maintained while a significant proportion of the absorption capacity of the lower density layer 5 is utilized

Alternative embodiments according to this aspect of the invention are shown in FIGS. 3 through 5. According to the second preferred embodiment in FIGS. 3 and 4, the higher density layer 6 extends as a strip along the entire length of the diaper. According to the third preferred embodiment shown in FIG. 5, the higher density layer 6 is coextensive with the entire lower density layer 5.

Yet another alternative to each of the embodiments described above is that of varying the pore size without necessarily varying the density. For example, the present inventor has discovered that the fine fiber dimensions of hardwood fluff can be utilized to advantage by substituting at least about 50%, and preferably about 80% to 100%, hardwood fluff fibers of approximately the same density as the lower density softwood fluff fiber layer 5 for the higher density softwood fluff fiber layer 6. This can be done because the hardwood fluff has a smaller pore size than the softwood fluff material. As a result, if hardwood fluff fibers are used as a replacement for the higher density softwood fluff fibers, two different pore size distributions will still be obtained within the scope of the invention, even if the density of each layer is the same. Thus, for example, a two component fluff sandwich comprising a coarse pore structure in the upper layer 5 obtained from a predominately softwood fluff pulp and a fine pore structure in the lower layer 6 comprised of a preponderantly hardwood fluff pulp fluff, densified throughout to one density (preferably approximately 0.1 g/cm³) can successfully be used with similar results to those obtained according to the embodiments described.

The second aspect of the invention relates to including a portion of superabsorbent material (SAM) 9 as part of the liquid absorbing material 4. The term "superabsorbent material" as used herein refers to one or more hydrocolloid materials capable of absorbing many times its own weight of water or aqueous fluid. These materials are generally prepared by polymerizing one or more monomers which, if homopolymerized by conventional methods, would form water soluble polymers. To render them water-insoluble and suitable for the present invention, these polymers or mixture of polymers are typically reacted, frequently with a crosslinking agent, to form crosslinked polymers, thereby introducing a limited water-insolubility while retailing susceptibility to swelling in water and water-containing fluids. Pseudocrosslinking may also be achieved by chain entanglement of high-molecular weight polymers, thus effecting water insolubility (see, e.g., U.S. Pat. No. 4,340,706). Typically, these hydrocolloids are salts of polyacrylic acid and variations thereof, such as methacrylic acid. Commercially they are available under the trademarks WATER LOCK J-500 from Grain Processing Co.; ABASORB 720 from Arakawa Chemical, (U.S.A.) Inc.; and Aqualic-CA from Mitsui Co. Alternative superabsorbents also may include hydrophilic polymer grafts onto starch or cellulose backbones and crosslinked carboxylated celluloses.

In FIGS. 6 and 7 the fourth preferred embodiment is shown wherein the superabsorbent material 9 is sandwiched between a first higher density component 10 and a second higher density component 11. As can be seen from reference to FIGS. 6 and 7, the superabsorbent material 9 is located more towards one of said end edges than the other. These first and second higher density components 10, 11 are disposed in an equivalent position to the higher density layer 6 in the first three embodiments discussed above. However, it is generally preferred that the superabsorbent material 9 is localized in an area 17 slightly above a region midway between the target area 7 and the upper edge 8. Thus, the superabsorbent material 9 provides an additional reservoir for liquid waste that has been drawn up the diaper by the higher density layer 6.

An important advantage of this aspect of the invention is that it assists in fluid distribution along the length of the superabsorbent material. Generally, superabsorbents 9 disposed in a fiber matrix enhance fluid distribution in the direction corresponding to the thickness of the liquid absorbing material 4. However, due to the swelling nature of the superabsorbent material 9, wicking in the plane of the fiber matrix bearing the superabsorbent 9 is severely hindered. According to this aspect of the present invention, wicking across the entire length of the superabsorbent material 9 is accomplished by sandwiching the superabsorbent material 9 between the first high density component 10 and the second high density component 11. Thus, the liquid waste is brought into contact across an upper surface 12 and a lower surface 13 of the superabsorbent material 9 rather than across a bottom edge 14 thereof. This is an improvement over border-to-border transfer of liquid waste, in much the same way as the first aspect of the invention, described in connection with FIGS. 1-5, provides the improvement of surface to surface contact between the lower density layer 5 and the higher density layer 6.

FIGS. 8 and 9 show an alternative embodiment wherein the superabsorbent material 9 is disposed adjacent the outer, liquid impermeable cover 3, and then covered with the single higher density layer 6 which is in turn covered with the lower density layer 5.

Of course, still further alternative embodiments are provided by using a softwood fluff pulp in the layer 5 and a hardwood fluff pulp in the layers 6 (FIGS. 8 and 9), or 10 and 11 (FIGS. 6 and 7), with uniform densification of all layers to about 0.1 g/cm³, or in the range of about 0.1 g/cm³ to about 15 g/cm³. Yet further variations within the scope of this invention include using a softwood fluff pulp of a first density in combination with a hard wood fluff pulp of a second density, wherein the second density is preferably higher than the first density.

The term "density" as used herein refers to the density of the composite structure of the lower density layer 5 or the higher density layer 6, and not the actual fiber density. (The actual fiber density is about 1.5 g/cm³.) The density of the lower density layer 5 should be in the range of about 0.03 to about 0.14 g/cm³, with the preferred range, in light of considerations of integrity and bulk, at about 0.07 to about 0.11 g/cm³. The higher density layer 6 should have a density in the range of about 0.14 to about 0.3 g/cm³, and preferably in the range of about 0.16 to about 0.22 g/cm³ for providing the desired capillarity without excessive stiffness. The density for of 0.2 psi. An important consideration in selecting suitable ranges for the higher density fluff and lower density fluff is that although there should be two distinct pore size distributions, one for each of the respective layers of fluff, these pore size distributions should overlap because this will permit flowback from the high density layer back to the low density layer.

The densified layer 6 may be a multiple ply layer rather than merely a single ply layer, and the ply may increase in density across the width or length of the layer 6 within the specified range or can be of uniform density. The basis weight of the lower density layer 5 should be in the range of about 150 to about 500 g/m² to provide the desired aesthetic appearance and comfort of the diaper. The basis weight of the higher density layer 6 should be in the range of about 150 to 1250 g/m².

It is preferred that the higher density layer 6 be substantially separately rather than integrally formed with the lower density layer 5, to achieve better moisture distribution therethrough. It should be noted, however, that the layers 5 and 6 are "substantially separately" formed even when formed in the same machine, one on top of the other, with some admixing at the interface. By the "substantial separate" terminology, it is intended only that two substantially discrete layers are formed, rather than a substantially single layer having a "skinned" surface, such as described in U.S. Pat. Nos. 2,952,260, 2,955,641, 3,017,304, 3,060,936, and 3,494,362 to Burgeni. Thus, densification should be achieved uniformly through the higher density layer 6, and care should be taken to avoid substantial skinning, where such skinning is as described in the Burgeni patents or in the Aberson U.S. Pat. No. 4,103,062. Skinning produces undue stiffness in the fluff and results in low absorbent capacity in the bonded (skinned) layer. Skinning can be prevented by avoiding excess moisture and by maintaining both platens at approximately the same temperature to avoid condensation through the thickness of the material. The present invention avoids the densification of the fluff to the point of forming a skin layer so that the densified fluff layer 6 retains at least about 80% void volume, resulting in significant absorbent capacity.

The layer 6 is densified in a heated press, such as can be obtained by Dake, Grand Haven, Michigan, as a "Dake Laboratory Press", Model No. 44-148 which includes heated platen operated under suitable conditions of temperature and pressure as known in the art to achieve the desired density. Alternatively, a heated calender nip is suitable for use in the densification process, as known in the art.

Comminuted wood pulp (fluff) is preferred for this invention, but other cellulose fibers such as cotton linters can be used. The preferred fluff is southern pine kraft wood pulp (i.e., made according to the sulfate process commonly known in the art) which has been bleached, such as can be purchased from ITT Rayoneer or International Paper Company. A suitable hardwood fluff pulp is southern hardwood kraft obtainable from Weyerhauser as "New Bern 309".

The superabsorbent material can be obtained from the Grain Processing Company of Muscatine, Iowa as their product Water Lock™ J-500 or A-100. Suitable inner liners 2 and outer covers 3 are easily obtained and well known in the art.

Of course, many changes and modifications can be made to the preferred embodiments described herein without departing from the spirit of the invention. For example, the densified fluff layer 6 could also be used with other absorbents such as coformed (meltblown polymer fibers combined with wood pulp and/or staple fibers) webs, carded webs, air-formed (staple wood pulp blends) webs and the like, at a lower density. Further, the absorbent structures described herein have applications to embodiments other than diapers, such as to sanitary napkins or other hygienic media. Therefore, it is intended that the preferred embodiments described in this specification be regarded as illustrative rather than limiting and it is intended that the claims, including all equivalents, define the scope of the invention.

The advantages resulting from this invention will be clearly understood with respect to the following examples and test data.

EXAMPLE I

The high density fluff was prepared by running the fluff into a hot calender nip (steel on hard rubber) at 250° F. at a speed of 10 ft/min. The nip pressure was sufficient to give a measured density on standing overnight of 0.15 g/cm³. Alternatively the fluff could have been pressed in a blotter lined platen press heated to about 250° F. for about 5 seconds, with sufficient pressure to achieve the desired fluff density.

The lower density fluff was prepared by passing it through a calender nip at 250° F. at a speed of 10 ft/min and sufficient pressure to achieve a measured density on standing overnight of 0.1 g/cm³.

In both cases the fluff was prepared from southern pine bleached kraft wood pulp, and was cut to dimensions such that the weight conditions set forth in Table I below were met. The combined low density fluff and high density fluff weight are given in the first column of Table I. The total absorbent weight was maintained at about 37 grams for each diaper, except for the one containing superabsorbent. The diaper with superabsorbent located as shown in FIG. 8 contained an additional 7 grams of superabsorbent composite consisting of about 3 grams of particulate superabsorbent (Water Lock™ A-100 from Grain Processing Co., Muscatine, Iowa; about 3 grams of polyolefin; and about 1 gram of porous nonwoven wrap. The composite was made in accordance with the teaching of Mazurak and Fries, as set forth in U.S. Pat. No. 4,381,782. The diaper construction was completed by sandwiching the absorbent composite between a porous spunbonded polypropylene liner (23 g/yd²) and a polyethylene film outer cover, sealed together with adhesive at the diaper perimeter. Five types of diapers were constructed in this fashion, corresponding to the diaper description of Table I.

Each of the diapers was then subjected to a 15 minute vertical wicking test with synthetic urine, followed by 15 minutes of equilibration out of contact with the urine bath. The results of this testing are shown in Table I and FIGS. 10-14.

In this test the preweighed diapers were mounted on a lucite plate (3/8"×13"×14") with the impervious poly backing adjacent the plate surface. The diaper was symmetrically wrapped around the edge of the plate with the longitudinal dimension of the diaper parallel to the long dimension of the plate. The waist line edges of the diaper were mounted on the plate with masking tape, the elastic leg bands being cut in 2 or 3 places to facilitate the mounting.

The plate was suspended vertically over a fluid bath contained in a glass tray with the longitudinal dimension of the diaper perpendicular to the fluid surface. The fluid was then brought into contact with the lower edge of the diaper so that the diaper edge was slightly immersed, and was maintained in this position for 15 minutes. The diaper was then removed from fluid contact and allowed to hang in the same vertical orientation for 15 minutes equilibration. The fluid used for the diapers in Table I was a synthetic urine composed of by weight 1% urea, 0.01% Pluronic 10R8 surfactant to bring the surface tension to about 56 dynes/cm, and 0.04% sodium azide preservative.

After equiliberation the diapers were removed from the plate and weighed and the fluid pick up noted. The results are summarized in Table I and represent the average of seven measurements on each diaper design.

After weighing, the diapers were laid horizontally on a 3"×15" cutting die which was segmented into 9, 1.7-inch zones with cutting edges across the die width as well as the outer perimeter. Several quick blows with a wooden mallet divided the 3-inch wide absorbent strip along the longitudinal axis of the diaper into 9 segments. The absorbent component in each segment was weighed, oven dried and reweighed and the fluid pick up determined on a gram per gram or fiber basis (corrected for deposited solids from the fluid).

In the case of the diaper with the superabsorbent pouch, the synthetic urine composition was adjusted to more closely simulate the electrolyte composition of baby urine, namely: 0.31 g. CaH₄ (PO₄)₂ H₂ O, 0.68 g. K H₂ PO₄, 0.48 g. MgSO₄ 7H₂ O, 1.33 g. K₂ SO₄, 1.24 g. Na₃ PO₄ 12H₂ O, 4.4 g. NaCl, 3.16 g.KCl, 0.4 g. NaN₃, 8.56 urea and 0.1 g. Pluronic 10R8 per liter, using distilled water as the solvent. The components were added to 900 mls of distilled water in the order given and each dissolved before the next component was added, and finally diluted to 1 liter.

The dotted curve in FIG. 10 represents the equilibrium capacity for the low density fluff at the indicated hydrostatic tensions as measured in a capillary tension cell. It is apparent that only at short wicking distances (4.5 cm) does the fluff reach its ultimate capacity. At the greater wicking heights (9-18 cms) it is well below its capacity.

FIGS. 11-13 demonstrate the ability of the densified fluff layer to pull the fluid up against the hydrostatic heads indicated. Comparison of the fluid level in the low density fluff in the back of the diaper with that in the same material in front at the corresponding head is a measure of the effectiveness of the high density fluff to improve the utilization of the low density material (e.g. 2.8 g/g back vs. 0.1 g/g front at 18 cms head, FIG. 13).

FIG. 14 shows the effectiveness of the densified layers in carrying and transferring fluid to the superabsorbent. The levels of fluid pickup in the superabsorbents are 12 and 22 g/g respectively at the 9 and 13.5 cm heads. Comparing this to FIG. 12 illustrates the effectiveness of the superabsorbent in diverting fluid from the fluff components at the highest heads.

It is apparent from these results that fluid distribution is greatly enhanced up the back of the diaper in the designs with densified fluff layers. The contrast with the fluid distribution in the front of the diaper, where densified fluff layer is absent, is very evident from the figures. Of course, better fluid distribution in the front as well as the back of the diapers would be obtained when the second and third preferred embodiments are followed. However, the first preferred embodiment was followed for the purposes of these tests because the diaper front tends to become fairly thoroughly wetted when the release of waste fluid occurs when the child wearing the diaper is lying on its stomach, for example when it is sleeping.

Moreover, the results demonstrate that the fluid distribution in the low density fluff areas is significant. This demonstrates the unexpected synergism obtainable in these designs.

In the instance of the superabsorbent diaper, which was made in accordance with the fourth embodiment set forth in this specification, the superabsorbent material drained substantial fluid from the higher regions of the diaper. However, these regions toward the upper edge 8 of the diaper provide surplus absorbing capacity if needed.

                                      TABLE I                                      __________________________________________________________________________     Whole Diaper Vertical                                                          Wicking Test*                                                                             Absorbent                                                                            Weight of                                                                              Amt. of                                                                               Fluid Ab-                                                 Weight                                                                               Comp. Fluff                                                                            Fluid  sorbed Over                                    Diaper Description                                                                        g.    g.      Absorbed g.                                                                           Control %                                      __________________________________________________________________________     Control Diaper                                                                            36     0      140    --                                             Diaper containing 1                                                                       38     7      171    22                                             ply of compressed                                                              fluff                                                                          Diaper with 2 plies                                                                       37    14      191    37                                             of compressed fluff                                                            Diaper with 3 plies                                                                       35    21      203    45                                             of compressed fluff                                                            Diaper with 2 plies                                                                        43** 14      215    54                                             of compressed fluff                                                            & SAM                                                                          __________________________________________________________________________      *Absorption time: 15 minutes followed by 15 minutes equilibration time.        **Contains 7 g. of assembly containing 3 g. SAM.                         

EXAMPLE II

The present inventor has discovered that similar functionality to the higher density fluff can be achieved with finer fiber, hardwood pulp fluff but at normal density (0.1 g/cm³). This discovery was made following the observation of a remarkable similarity in the pore volume distribution of 0.1 g/cm³ density hardwood fluff and that of 0.2 g/cm³ softwood fluff. The following tables compare the vertical wicking properties of softwood and hardwood fluff.

The vertical wicking test was somewhat similar to that conducted with whole diapers described above. This test was conducted on 3"×15" strips of the absorbent material mounted on a 3/8"×5'×14" lucite plate in the same orientation and manner described for the diapers. A nylon mesh screen was used to support the fluff strip on the lucite (acrylic) plate. The plate and strip were then suspended from weight-sensing means such as a load cell in an Instron tensile tester. The synthetic urine (in these cases the second or salt-containing formulation) was then put in contact with the lower edge of the absorbent strip and the amount of fluid absorbed as a function of time is recorded at several time intervals for the 15 minute duration of the test. The amount absorbed was calculated as the grams per unit basis weight of 1 gm/cm² per unit width (1 inch). The vertical wicking capacity is defined as the amount absorbed in the defined units at the end of the 15 minute test. The reported rate was that measured from the plot of amount absorbed/unit basis weight/unit width versus time^(1/2) over the time interval of 7-21 seconds. The test was replicated six times and the results reported are averages of these six measurements.

Fluid distribution in this test was measured by die cutting the sample immediately following the completion of the test, the same manner described for the whole diapers. In this case zones corresponding to the same vertical heights were combined to give the results shown in Table III.

As may be concluded from the results in Table II, the vertical wicking capacity of 0.1 g/cm³ density hardwood fluff corresponds closely with that of 0.2 g/cm³ density softwood fluff. The initial wicking rate of the hardwood fluff falls between the two softwood fluffs. The fluid distribution pattern in Table III also shows the similarity of the hardwood fluff and the 0.2 g/cm³ density softwood fluff. These results imply a slightly larger average pore size for the former than the latter.

Hence, a combination of softwood and hardwood fluff at 0.1 g/cm³ density should have similar fluid distribution properties to a two-density sandwich of softwood fluff, as previously described in this disclosure.

                  TABLE II                                                         ______________________________________                                         VERTICAL WICKING CAPACITY/RATE                                                 (Showing similarity in capillarity of softwood kraft at                        0.2 g/cm.sup.3 and hardwood kraft at 0.1 g/cm.sup.3 density)                                      *Vertical                                                             Density  Capacity   Wicking Rate                                     Material  (g/cm.sup.3)                                                                            G/UBW/UW   G/UBW/UW/SEC.sup.1/2                             ______________________________________                                         Softwood Kraft                                                                           0.1      499        48                                               Fluff                                                                          Softwood Kraft                                                                           0.2      573        36                                               Fluff                                                                          Hardwood  0.1      580        42                                               Kraft Fluff                                                                    ______________________________________                                          *Units are grams per unit basis weight (1g/cm.sup.2) per unit width (1         inch).                                                                   

                  TABLE III                                                        ______________________________________                                         FLUID DISTRIBUTION IN VERTICAL WICKING                                                  **Specific Absorbency (g/g)                                                    at Following Tensions                                                          0 cm  4.5 cm  9 cm    13.5 cm                                                                               18 cm                                    ______________________________________                                         Softwood Kraft                                                                            9.0     9.0     6.4   3.0    0.7                                    (0.1 g/cm.sup.3)                                                               Softwood Kraft                                                                            6.0     6.1     5.8   5.0    4.7                                    (0.2 g/cm.sup.3)                                                               Hardwood Kraft                                                                            8.2     8.1     7.2   5.3    3.3                                    (0.1 g/cm.sup.3)                                                               ______________________________________                                          **Tensions are measured as vertical distance from fluid source.          

EXAMPLE III

This example is directed to a double fluff layer of softwood fluff over hardwood fluff. The hardwood fluff was a bleached kraft, South American Eucalyptus hardwood pulp. The two-ply fluff contained equal weights of the softwood and hardwood pulp layers. After densifying the layers to 0.1 g/cm³ density, the vertical wicking properties (same test procedure as for example II) were as follows:

                  TABLE IV                                                         ______________________________________                                         VERTICAL WICKING PROPERTIES OF                                                 SOFTWOOD/HARDWOOD LAYERED BATT                                                                   ***Specific Absorbency                                       ***Vertical                                                                            ***Wicking                                                                               At Following Tensions                                        Capacity                                                                               Rate      0 cm   4.5 cm                                                                               9 cm 13.5 cm                                                                               18 cm                               ______________________________________                                         544     46        7.8    7.8   6.1  4.3    3.0                                 ______________________________________                                          ***Same units as in Tables II, III.                                      

Comparing the distribution results for the double-layered fluff in Table IV with those for softwood kraft (Table III), it is apparent that the presence of the Eucalyptus layer greatly improves fluid wicking against the upper two hydrostatic heads (i.e. in the 13.5 cm and 18 cm zones). This is particularly impressive since the Eucalyptus only represents 50% of the two-ply structure.

EXAMPLE IV

A 40 g/m² web of meltblown polypropylene containing 40 percent by weight of superabsorbent (Waterlock J-500 from Grain Processing Company) was prepared. The superabsorbent was intermixed with the fine meltblown fibers (surface area about 1 m² /g) containing enough surfactant (e.g., about 0.3-0.5 percent Triton X-102 from Rohm & Haas Company) to assure wetting of the fiber matrix, the composite being densified to 0.1 g/cm³ during the manufacturing process.

When this web was subjected to the vertical wicking procedure described in Example II, the results presented in Table 5 were obtained. From these results it is apparent that the fluid wicks vertically 4.5 cms but then essentially stops, presumably because the swelling particles have restricted the fluid flow in the web by plugging the pores.

When this same web was placed beneath a softwood fluff layer, having a density of 0.2 g/cm³, in a diaper construction, and the whole diaper was subjected to the vertical wicking test (described in Example I), the effect of the fluff layer as a fluid distributor for the superabsorbent was apparent. In Table 6, the fluid distribution is shown for the total absorbent composite, the fluff layer itself, and for the meltblown/superabsorbent web.

Comparing the vertical distribution for the meltblown/superabsorbent web from the diaper (Table 6) with the data in Table 5, it is apparent that the densified fluff acts to wick the fluid higher and improves the distribution to the superabsorbent (compare at 9 cm height, 11.6 g/g vs. 1.1 g/g; and at 13.5 cm height, 2.7 g/g vs. 0.1 g/g). Note that both tests were similarly run for 15 minutes. Furthermore, if the tests were allowed to proceed further, the height wicked in the diaper would continue to increase, whereas wicking in the superabsorbent web alone would virtually stop.

                                      TABLE 5                                      __________________________________________________________________________     VERTICAL WICKING TEST                                                          MELTBLOWN/SUPERABSORBENT WEB                                                            Basis    ***Specific Absorbency                                                Weight                                                                             Density                                                                             at Following Tensions*                                       Description                                                                             g/m.sup.2                                                                          g/cm.sup.3                                                                          0.0 cm                                                                             4.5 cm                                                                             9.0 cm                                                                             13.5 cm                                                                             18.0 cm                                     __________________________________________________________________________     Meltblown Web                                                                            93 0.1   7.9                                                                               7.7 2.4 0.0  0.0                                         with No Super-                                                                 absorbent                                                                      Meltblown Web                                                                           139 0.1  23.0                                                                               20.5                                                                               1.1 0.1  0.0                                         with 40% Super-                                                                absorbent                                                                      __________________________________________________________________________      *Hydrostatic Tension in cm. of water.                                          ***Same units as in Tables II and III.                                   

                                      TABLE 6                                      __________________________________________________________________________     VERTICAL WICKING TEST                                                          ON DIAPER CONTAINING                                                           MELTBLOWN/SUPERABSORBENT WEB                                                                            ***Specific Absorbency                                          Dry Absorbent                                                                          Absorbent                                                                             at Following Tensions*                                Diaper Absorbent                                                                         Weight (g.)                                                                            Component                                                                             0.0 cm                                                                             4.5 cm                                                                             9.0 cm                                                                             13.5 cm                                                                             18.0 cm                              __________________________________________________________________________     Fluff densified                                                                          42.7    Fluff  7.5  7.2                                                                               4.5 2.5  1.5                                  to 0.2 g/cm.sup.3 over                                                         coextensive layer MB/SAM**                                                                              18.8                                                                               19.7                                                                               11.6                                                                               2.7  1.0                                  of Meltblown Web                                                               with 40%          Combined                                                                              9.9 10.1                                                                               6.4 2.6  1.5                                  Superabsorbent    Absorbent                                                    (basis weight 139                                                              g/m.sup.2)                                                                     __________________________________________________________________________      *Hydrostatic Tension, cms of water                                             **Meltblown Web/Superabsorbent                                                 ***Same units as in Tables II and III.                                    

I claim:
 1. A disposable absorbent article for absorbing body fluids, said absorbent article having end edges at opposite ends of the length of the absorbent article, said absorbent article comprising:a body facing liquid-permeable liner; an outer liquid-impermeable cover; and liquid-absorbing materials located between said liner and the cover, said liquid-absorbing materials comprising hydrophilic fibers and a water-insoluble superabsorbent material, said liquid-absorbing material defining:a target area where liquid waste initially accumulates; and a reservoir containing superabsorbent material which superabsorbent material is located more towards one of said end edges than the other and is localized in an area laterally removed from said target area; wherein said target area has a lower average density and a lower basis weight than said reservoir.
 2. A disposable absorbent article according to claim 1, wherein said liquid absorbing materials have a mean density greater than about 0.03 grams per cubic centimeter and less than about 0.3 grams per cubic centimeter.
 3. A disposable absorbent article according to claim 1, wherein the reservoir comprises a mixture of hydrophilic fibers and superabsorbent material.
 4. A disposable absorbent article according to claim 3, wherein the target area consists essentially of hydrophilic fibers.
 5. A disposable absorbent article according to claim 1, wherein the reservoir is preponderantly found within 1/2 o f the length of said absorbent article which includes one of said end edges.
 6. A disposable absorbent article according to claim 5, wherein the reservoir comprises a mixture of hydrophilic fibers and superabsorbent material.
 7. A disposable absorbent article according to claim 6, wherein the target area consists essentially of hydrophilic fibers.
 8. A disposable absorbent article according to claim 3, wherein said superabsorbent material is predominantly found within 1/2 of the length of said absorbent article which includes one of said end edges.
 9. A disposable absorbent article according to claim 5, wherein said reservoir is predominantly found within 1/2 of the length of said absorbent article which includes one of said end edges.
 10. A disposable absorbent article according to claim 1, wherein said target area comprises an upper layer underlying said liner, and said reservoir includes a lower layer underlying said upper layer.
 11. A disposable absorbent article according to claim 10, wherein said lower layer comprises a substantially uniform mixture of hydrophilic fiber material and superabsorbent material.
 12. A disposable absorbent article according to claim 11, wherein said superabsorbent material is present in said lower layer in an amount of from about 14% to about 50% by weight.
 13. A disposable absorbent article according to claim 12, wherein said target area has a density of from about 0.03 to about 0.14 grams per cubic centimeter.
 14. A disposable absorbent article according to claim 1, wherein the density of said liquid absorbing materials varies across the width of the absorbent article.
 15. A disposable absorbent article according to claim 1, wherein the density of said liquid absorbing materials varies along the length of the absorbent article.
 16. A disposable absorbent article according to claim 1, wherein said reservoir has a basis weight in the range of about 150 to about 1,250 grams per square meter.
 17. A disposable absorbent article according to claim 16, wherein the target area has a basis weight in the range of about 150 to about 500 grams per square meter.
 18. A disposable absorbent article according to claim 1, wherein said hydrophilic fiber is cellulose fiber.
 19. A disposable diaper having end edges at opposite ends of the length of said diaper, said diaper comprising:a body facing liquid-permeable liner; an outer liquid-impermeable cover; and liquid-absorbing materials located between said liner and cover, said liquid-absorbent materials comprising hydrophilic fibers and a water-insoluble superabsorbent material, said liquid-absorbing materials defining:a target area where liquid waste initially accumulates; and a reservoir containing superabsorbent material, which superabsorbent material is located more towards one of said end edges than the other and is localized in an area laterally removed from said target area; wherein said target area has a lower average density and a lower basis weight than said reservoir. 